Polyether Polyols mo PU Adhesives & Sealants
Vasega | Fauga | Fa'amatalaga | |||||
OH Taua | Viscocity | vai vai | Fa'atinoga | Molecular Weight | Fa'atatauga | ||
mgKOH/g | mpa·S/25℃ | % | g/mole | ||||
PF-040 | Glycerol Propoxy | 450±30 | 360±100 | ≤0.05 | 3 | 375 | Mea fa'apipi'i/Sulu foam/So'i feso'ota'i |
PF-450 | Glycerol Propoxy E tutusa ma Voranol CP 450 | 380±15 | 330±30 | ≤0.05 | 3 | 450 | Ufiufi/Fofolaga/Tu'u Fa'amea/Fa'apipi'i |
PF-1050 | Glycerol Propoxy | 170±10 | 250±50 | ≤0.05 | 3 | 1000 | Ufiufi/Fofolaga/Tu'u Fa'amea/Fa'apipi'i |
PF-2080 | Propandiol Propoxy | 14±1.5 | 3000±500 | ≤0.05 | 2 | 8000 | Fa'apipi'i/Sealants/Elastomers |
PF-2120 | Propandiol Propoxy | 9.5±1.5 | 6000±2000 | ≤0.05 | 2 | 12000 | Fa'apipi'i/Sealants/Elastomers |
Hydrophillic Polyether Polyols
Vasega | Fauga | Fa'amatalaga | |||||
OH Taua | Viscocity | vai vai | Fa'atinoga | Molecular Weight | Fa'atatauga | ||
mgKOH/g | mpa·S/25℃ | % | g/mole | ||||
PF-3500 | Glycerol Propoxy Ethoxy E tutusa ma Voranol CP1421 | 35±2 | 1200±300 | ≤0.05 | 3 | 5000 | Fa'agogo malūlū ma hypersoft fetu'utu'una'i slabstock /Sela tatala/Viscoelastic foams |
PF-010 | Glycerol Propoxy Ethoxy E tutusa ma le IP 010 | 22±1 | 2200±300 | ≤0.05 | 3 | 8000 | Suia MDI/Hidrophilic polyuerthanes |
Isi Polyether Polyols Faapitoa
Vasega | Fauga | Fa'amatalaga | |||||
OH Taua | Viscocity | vai vai | Fa'atinoga | Molecular Weight | Fa'atatauga | ||
mgKOH/g | mpa·S/25℃ | % | g/mole | ||||
PF-2802 | Propandiol Propoxy Ethoxy E tutusa ma Voranol EP 1900 | 28±1.5 | 800±200 | ≤0.05 | 2 | 4000 | High reactive, Fa'alelei loimata sthength mo seevae seevae |
Y-950 | TOFP Trimethylolpropane oxide propylene eter | 950±50 | 6750±750 | ≤0.05 | 3 | 180 | Malosi fa'ainisinia maualuga mo Mea Fa'atasi |
PF-3075 | Trimethylolpropane oxide propylene eter | 750±20 | 5750±750 | ≤0.05 | 3 | 220 | |
PF-628 | Sorbitol Propoxy Ethoxy Voranol HF505 | 28±2 | 1600±200 | ≤0.05 | 6 | 12000 | Toe fa'aleleia maualuga ma fa'amafanafanaga mo fa'ama'i fa'ama'i a HR slabstock/latex |
PF-R800 | AEEA Propoxy | 800±30 | 17000±2500 | ≤0.05 | 4 | 280 | Auto-catalytic vave fa'afofoga mo Malosi foam/Api'i/tu'u |
Sili Polyethylene Glycols
Vasega | Fauga | Fa'amatalaga | |||||
OH Taua | K+ | Fa'aaliga | Fa'atinoga | Molecular Weight | Fa'atatauga | ||
mgKOH/g | ≤ppm | g/mole | |||||
PEG1000 | 105-120 | 5 | Suavai | 2 | 1000 | Textiles: O loʻo faʻaaogaina le PEG i fale gaosi oloa mo faʻaoga eseese e pei o le antistat, lubricant, faʻamamaina, lelei, emulsifier, mea mata mo le valiina, vaeluaga mo le togafitia o sui, ma isi.Paʻa: E pei o le PEG o loʻo i ai le hydrophilicity lelei, e faʻaaogaina e fai ma sui faʻamalolo mo le foam Rubber, Latex Rubber, ma isi. Uamea: O le PEG e faʻaaogaina e avea o se mea mataʻutia i totonu o se nofoaga e taofia ai le pala mo uʻamea, faʻamaʻi, ma isi.Ma e faʻaopoopoina i se abrasive e faʻaleleia ai le aʻafiaga o Pelp & Pepa abrasive. | |
PEG2000 | 54.5-57.5 | 5 | Malosi | 2 | 2000 | ||
PEG3000 | 32-35 | 5 | Ma'a'ai | 2 | 3000 | ||
PEG6000 | 18-19 | 5 | Ma'a'ai | 2 | 6000 | ||
PEG10000 | 10.2-12.5 | 5 | O le pauta | 2 | 10000 | ||
PEG20000 | 5-6.2 | 5 | O le pauta | 2 | 20000 |
Polyol fa'afefiloi
Vasega | Vaega | Fa'amatalaga | ||
MPF-408 | Polyether polyols po'o polyester polyols po'o le TCPP 50 ~ 80%,HFC-245fa 20~50% | Fa'apitoa e tusa ai ma mana'oga o tagata fa'atau | ||
MPF-508 | Polyether polyols 64%,Cyclopentane 36% | Fa'apitoa e tusa ai ma mana'oga o tagata fa'atau | ||
MPF-4141 | Polyether polyols po'o polyester polyols 50%,HCFC-141b 50% | Fa'apitoa e tusa ai ma mana'oga o tagata fa'atau |